Sliding wear behavior of FeCrC reinforced and Ni-based composites produced by mechanical alloying technique
vol. 56 (2018), no. 1, pp. 65 - 74

The study presents the behavior of FeCrC particulates reinforced and Ni-based composites produced by a mechanical alloying process in the presence of friction and wear. Ni, Al and M7C3 powders having 100 μm size were mixed, mechanically alloyed and the compacts were sintered in an atmosphere controlled furnace. The mechanically alloyed (MAed) samples were investigated by SEM, EDS and DTA. For the wear tests, the samples were tested in dry conditions. The worn surfaces were examined using OM to study the wear behavior. The friction coefficient was recorded continuously during the wear test and wear rate. The highest wear rate was obtained at 800 °C, and the lowest was obtained at 900 °C. With the increase of reinforcement amount, wear rate decreased.

Key words
metal matrix composites, mechanical alloying, abrasion, thermal analysis

[open article.pdf] Full text (1537 KB)

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.6.9      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.

Article abstracts updated: 2019-04-11 17:21      
Articles in press revised: 2019-04-15 12:50     
Full text pdf uploaded: 2019-03-15 10:41    
Information updated: 2018-08-18 11:39   
Code last revised: 2017-12-22 14:57  

© OldSoft, 2004, …, 2019