Fracture analysis of AZ6-F magnesium composite materials at quasi-superplastic state
BESTERCI, M., HUANG, S.-J., SÜLLEIOVÁ, K., BALLOKOVÁ, B., VELGOSOVÁ, O.
vol. 55 (2017), no. 3,

Abstract
Micromechanisms of fracture of AZ61-F composites in the zone of quasi-superplastic deformation were analysed and quantified in this work. Deformation of AZ61-F magnesium alloys with 1 wt.% of Al2O3 phase was tested at a temperature of 473 K and different strain rates. It was shown that at the temperature of 473 K and the highest strain rate applied from 1 × 10–2 to 1 × 10–4 s–1, a significant growth of ductility was observed. The mean dimples diameter of the ductile fracture decreased with decreasing strain rate. The grain size of 0.7 μm was reached by severe plastic deformation using equal channel angular pressing (ECAP). Secondary Mg17Al12 and Al2O3 phases were identified. The maximum strain was obtained at the temperature of 473 K and strain rate of 1 × 10–4 s–1.

Key words
AZ61-F Mg-Al2O3, fracture analysis, quasi-superplastic behaviour, kinetics process

Full text not available

[IMMS SAS]      UMMS SAV - Bratislava (SK)   ver. 1.6.0   (oš)        [go to HOME PAGE]

Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.


Article abstracts updated: 2017-05-17 13:57     
Articles in press revised: 2017-04-24 13:42    
Full text pdf uploaded: 2017-04-05 09:52   
Information updated: 2017-05-10 17:18  

© OldSoft, 2004, …, 2017