Microstructure characterization of melt spun Mg65Cu225Y10
vol. 55 (2017), no. 1, pp. 1 - 5

Mg65Cu225Y10 ribbons were produced by melt spinning. Their microstructure was investigated in its as-cast condition, after pressing under 0.5 GPa for 5 min under different temperatures – RT, 50, 100, 150, and 200 °C – and after 5-minute exposure to the above temperatures without pressing. The microstructure was characterized by means of XRD, DSC, HRSEM, and HRTEM. XRD and DSC studies showed that the as-cast material had an amorphous character and that the material crystallized during exposure to temperature with or without applying stress. HRTEM revealed that the as-cast Mg65Cu25Y10, although known to be one of the best glass formers, is nano-crystalline rather than amorphous.

Key words
microstructure, melt spinning, metallic glass, Mg65Cu225Y10

[open article.pdf] Full text (365 KB)

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.6.9      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.

Article abstracts updated: 2018-11-27 09:39      
Articles in press revised: 2018-12-05 13:20     
Full text pdf uploaded: 2018-11-27 13:22    
Information updated: 2018-08-18 11:39   
Code last revised: 2017-12-22 14:57  

© OldSoft, 2004, …, 2018