Microstructure and strength of diffusion bonded joint between nickel aluminide Ni75Al25 and AISI 316L stainless steel using a nickel interlayer
TORUN, O., CELIKYUREK, I.
vol. 47 (2009), no. 4, pp. 263 - 267

Abstract
Diffusion bonding between nickel aluminide Ni75Al25 and 316 L austenitic stainless steel using a nickel interlayer was carried out at 1000 °C under vacuum for various hold times. The microstructures of the interface of joints were analysed by optical and scanning electron microscopy (SEM). Micrographs demonstrated that excellent bonding formed continuously along the interface. Chemical compositions of the interface of the bonded samples were determined using energy dispersive spectroscopy (EDS) and X-ray mapping studies were made on the fractured surface of all the specimens. Analysis results showed that reaction occurred between the base metals and the nickel interlayer. After welding process, shear tests applied to the bonded samples to determine shear strength of joints. Test results indicated that the maximum shear strength was 238 MPa for the bonded sample treated for 4 h.

Key words
nickel aluminides, stainless steel, bonding, electron microscopy

[open article.pdf] Full text (336 KB)

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.7.2      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.


Article abstracts updated: 2021-01-15 08:18      
Articles in press revised: 2020-10-30 12:09     
Full text pdf uploaded: 2020-11-09 13:07    
Information updated: 2020-06-29 17:09   
Code last revised: 2020-06-29 16:48  

© OldSoft, 2004, …, 2021