Influence of temperature exploitation on the failure of austenitic stainless steel (in Slovak)
BLACH, J.
vol. 38 (2000), no. 5, pp. 315 - 328

Abstract
17Cr-12Ni-2.2Mo commercial unstabilised austenitic steel of AISI 316 type was additionally annealed in the temperature range from 620 to 720 °C for 0.5 to 20 hours after the solution annealing. Cracks perpendicularly oriented to the magistral fracture, so called splitting, were observed on fracture surfaces of selected samples after the tensile tests at room temperature. The intergranular character of these cracks was identified by fractography analysis. The presence of secondary phase particles on grain boundaries was revealed by metallographic observations. The chemical nature of Cr-rich M23C6 carbides of the particles extracted into the carbon replicas were proved by means of TEM and EDX. Correlations between the amount of splitting and the temperature and holding time of annealing and the temperature of tensile test (-196 to 400 °C) was shown.

Key words
austenitic steel, tensile stress, intergranular cracks, intergranular fracture, intergranular carbides

Full text not available

[IMMS SAS]      UMMS SAV - Bratislava (SK) Personal data Protection   ver. 1.8.0      [go to HOME PAGE]
Full title of this journal is bilingual: Kovové materiály - Metallic Materials.
The official abbreviation in accordance with JCR ISI is Kovove Mater.


Article abstracts updated: 2023-10-26 07:45      
Articles in press revised: 2024-03-26 11:42     
Full text pdf uploaded: 2023-11-08 06:53    
Information updated: 2023-04-19 16:14   
Code last revised: 2024-03-06 11:13  

© OldSoft, 2004, …, 2024